How to deal with the cracks in Shandong aluminium alloy die castings? The following is a brief introduction for you.

　　一、可能的缘由剖析

　　I. Analysis of Possible Reasons

　　铝合金压铸件呈现裂纹的缘由有很多，其中有冷裂，热裂，材料缘由等原因都是这些因素。剖析结果，这次的产品设计中，呈现了一些薄壁的地方，裂纹常常呈现在这个位置。并且还发现了运输过程中的粗暴举动，磕磕碰碰也不少，也形成很多的裂纹。

　　There are many reasons for cracks in aluminium alloy die castings, including cold cracks, hot cracks, material reasons and so on. The analysis results show that in this product design, there are some thin-walled areas where cracks often appear. And also found in the transport process of rough behavior, bumps and collisions are many, but also formed many cracks.

　　二、压铸工艺上的改良措施

　　II. Improvement Measures in Die Casting Technology

　　铝合金压铸裂纹缺陷高，是由多种因素造成的，因此有必要同时采取措施。在模具上，薄壁位置加筋。也有关于在运输途中发生暴行的报告。

　　The high crack defect of aluminium alloy in die casting is caused by many factors, so it is necessary to take measures at the same time. On the die, the thin wall position is reinforced. There are also reports of atrocities in transit.

　　第三，改善效果

　　Third, improve the effect

　　改进后，裂纹缺陷的萌生性得到改善。

　　After improvement, the initiation of crack defects is improved.

　　以上是山东铝合金压铸裂纹的处理方法，希望本文能为您带来帮助。我们的网站是http://www.jnhjgs.cn

　　The above is the treatment method of Shandong aluminium alloy die casting cracks, I hope this article can help you. Our website is http://www.jnhjgs.cn.